Cast Milled plates in alloy 5083

Precision milled plates in alloy 5083 with PVC protection film.
Thickness from 8 up to  50 mm,
Thickness tollerance +/- 0.1
Roughness (μM) ≤0.4

SIFEMNMGCUZNCRTI+ZR
Min--0,404,0--0,5-
Max0.400,401,04,90,100,250,250,15

Tensile strength RmYield strength RP 0.2ElongationA [%]Hardness Brinnel
230-290 [MPA]110-130 [MPA]10-15%68-75 HB
WeldabilityAnodizingMalleabilityCorrosion resistance
++++++++++++

Larghezza mmLunghezza mmPeso Kg
15203020
20204020
22204520
25005000

Cast Slabs in alloy  EN AW 5083 (H0)

Alloy furnished  in an H0 (annealed) and homogenized state, high malleability, good for many uses, ideal for Mechanical applications.
Thickness fomr 3 mm up to 1100 mm.
Max width: 2.650 mm
Max length: 8.500 mm

SIFEMNMGCUZNCRTI+ZR
Min--0,404,0--0,5-
Max0.400,401,04,90,100,250,250,15

Tensile strength RmYield strength RP 0.2ElongationA [%]Hardness Brinnel
230-290 [MPA]110-130 [MPA]10-15%68-75 HB
WeldabilityAnodizingMalleabilityCorrosion resistance
++++++++++++

600x 1550 x 3100 mm
600x 1650 x 4700 mm
600x 1850 x 8000 mm
600x 2000 x 4000 mm
530 x 2130 x 8000 mm
700 x 2500 x 3800 mm
570 x 2560 x 7500 mm
1100 x 2150 x 3200 mm

Cast slabs in alloy EN AW 7021 T79

This alloy is perfect for moulds production, idonea alla costruzione di stampi, hydraulic industry and mechanical fabricating.

SIFEMNMGCUZNCRTI+ZR
Min--------
Max0,460,130,0971,280,045,610,020,038

Tensile strength RmYield strength RP 0.2ElongationA [%]Hardness Brinnel
320-380 [MPA]300-340 [MPA]2,5 - 4,5 %120 - 130 HBW [2,5/62,5]

1600 x 510 x 3000 mm
1600 x 600 x 3000 mm
2000 x 510 x 4000 mm