Bars  drawn and extruded 6082

This alloy shows medium mechanical characteristics, but exhibits problems when working with automatic lathes. In the case of large volume production, it is recommended to replace it with the Alloy 6092 (in compliance with 2000/53/EC – 2002/95/EC).
Used principally for forged and moulded parts, which must later, be subject to thermal treatment. 6082 complies with the European regulations 2002/95/EC ROHS) and 2000/53/EC (Automotive).

StatusT6
Ultimate tensile strength310 Rm N/mm2
Yield strength260 Rp 0,2N/mm2
Elongation to 5%10
Hardness Brinell95 HB
Density,2,71 Kg/dm3
Elastic modulus69.000 N/mm2
Thermal expansion coeff.24X10-6;/C
Thermal conductivity to 20°C167 w/mk
Electrical conductivity to 20°C0.037 m/Ωmm2
SIFECUMNMGCRNIZN
Min0.7--0.400.6---
Max1.30.500.101.001.20.250.200.10
Flat bars
10x370x550x8100x10120x12150x15180x2035x30100x35120x50
20x380x560x8110x10150x12180x15200x2040x30330x38130x50
30x3100x570x8120x10180x12200x15250x2050x3050x40150x50
40x320x680x8130x10200x12230x15300x2060x3060x40200x50
50x325x6100x8150x10250x12250x1530x2570x3070x40250x50
20x440x6150x8200x1025x1525x2040x2590x3090x4080x60
35x440x6150x8200x1025x1525x2040x2590x3090x4080x60
40x4450x615x10250x1030x1530x2045x25100x30100x4090x60
50x460x620x1020x1235x1535x2050x25120x30120x40100x60
60x480x625x1025x1240x1540x2060x25150x30130x40120x60
10x5100x630x1030x1245x1545x2070x25200x30150x40130x60
15x5120x635x1035x3250x1550x2075x25250x30160x40150x60
20x515x840x1040x1260x1560x2080x2540x35200x40200x60
25x520x845x1050x1270x1570x2090x2550x35300x4080x70
30x525x850x1060x1280x1575x20100x2560x3560x5090x70
35x530x860x1070x1290x1580x20120x2570x3570x50100x70
40x535x870x1080x12100x1590x20150x2580x3580x50120x70
50x540x880x1090x12120x15100x20200x2585x3590x3570x75
60x545x890x10100x12130x15160x20250x2590x35100x50100x80

Flat bars extra size

419x31250x50120x100
250x40200x60200x100
200x50120x80230x100

Square bars

10254570100150
12305080120160
15355585130180
20406090140200

Round bars

4075115170250330
42580120180260340
4585125190270350
5090130200280380
5595135210290400
60100140220300410
65105150230310500
70110160240320
Square bars
2025303540
45505560

Round bars

102542
153045
183550
203655
224060

Bars  drawn and extruded 6026

6026 is an alloy developed in response to the latest environmental standards. 6026 represents the best in tin alloys due to the fact that it is subject to the fragility and ruptures which submit them to pressures and high temperatures.

  • An alloy suitable for high speed mechanical processing.
  • 6026 is especially developed for the automobile sector
  • Exhibits an excellent anti corrosive property
  • Good aptitude to anodising decorative and hard
  • An alternative to alloys 6061, 6082, 6282, 6262 and 6012
StatusT6T8T9
Ultimate tensile strength310 Rm N/mm2345 Rm N/mm23360 Rm N/mm2
Yield strength260 Rp 0,2N/mm2315 Rp 0,2N/mm2330 Rp 0,2N/mm2
Elongation to 5%844
Hardness Brinell95 HB100 HB100 HB
Density2,62 Kg/dm3
Elastic modulus69.000 N/mm2
Thermal expansion coeff.23,4 X 10-6;/C
Thermal conductivity to 20°C172 w/mk
Electrical conductivity to 20°C26 m/Ωmm2
SIFECUMNMGCRZNTiBiPbSn
Min0.6-0,20.200.6---0,5--
Max1.40.700.51.001.20.30.300.201,5'.40.05
Square bars
50658095130160
557085100140200
607590110150

Round bars

406595125170230
4270100130180240
4575105135190250
5080110140200
5585115150210
6090120160220
Square bars
1018304560
12203550
15254055

Round bars

102542
153045
183550
203655
224060

Bars  drawn and extruded 2011

This alloy is especially recommended for processing with automatic lathes at high speed
and offers the following advantages:

  • excellent manoeuvrability with all types of tools
  • less resistance to the cut regarding all other alloys
  • longer tool duration
  • work area always clean due to presence of very fine metal shavings
  • good mechanical characteristics
  • possibility of anodising finished parts in different colours

The 2011 is the most recommended alloy for simple processing and at high speed

StatusT3T8
Ultimate tensile strength 320 Rm N/mm2370 Rm N/mm2
Yield strength 270 Rp 0,2N/mm2270 Rp 0,2N/mm2
Elongation to 5% 108
Hardness Brinell 90 HB110 HB
Density2,83 Kg/dm3
Elastic modulus70.000 N/mm2
Thermal expansion coeff.22,94X10-6;/C
Thermal conductivity to 20°C151 172 w/mk
Electrical conductivity to 20°C23 ÷ 26 m/Ωmm2
SIFECUMNMGCRZNTiBiPb
Min--5.0-----0,2-
Max0,40.706.0---0.30-0,60.4
Square bars
104575105150
205080110160
255585115180
306090120200
356595130
4070100140

Round bars

514223038455259
615233139465360
7193075115170260400
8203580120180270440
9214082125185280450
10224585130190290454
11235090135200300500
12245292140210320550
14255595145220320550
152660100150230350
162765105155
Square bars
5172870107,95160240360
6182972110165250380
7193075115170260400
8203580120180270440
9214082125185280450
10224585130190290454
11235090135200300500
12245292140210320550
14255595145220330600
152660100150230350
162765105155

Round bars

5172870107,95160240360
6182972110165250380
7193075115170260400
8203580120180270440
9214082125185280450
10224585130190290454
11235090135200300500
12245292140210320550
14255595145220330600
152660100150230350
162765105155

Bars  drawn and extruded 7075

This alloy exhibits good manoeuvrability and good mechanical characteristics. The machined details exhibit a smooth and brilliant surface with a good resistance to corrosion and may be submitted to hard anodising and protection.

This alloy is offered with a Pb content <1% and is therefore compliant with the requirements of the regulation 2000/53/EC.

StatusT60 e spessoriT6
Ultimate tensile strength560 Rm N/mm2=672 Rm N/mm2
Yield strength500 Rp 0,2N/mm2mm-N/mm^2650 Rp 0,2/mm2
Elongation to 5%7Ø 50 ÷ 180
8
Hardness Brinell 140 HB168 HB
Density2,80 Kg/dm3
Elastic modulus 72.000 N/mm2
Thermal expansion coeff.23,5 20 ÷ 100 C x 10 -%C
Thermal conductivity Status W/mkT6 172
Specific heat 0 ÷ 100°C - Cal./g°C0,23
Electrical resistivity - Stato Ohm mm^2mmT6 0,033
Melting point - Aproximate °C range580 ÷ 650
SIFECUMNMGCRZNTiBiPb
Min--1,20.40.60.185.1---
Max0,40.502,01.01.20.286.10.2--
Square bars
15356090140200
20406595150220
254270100160230
284575110170250
305080120180
325585130190

Round bars

SIFECUMNMGCRZNTiBiPb
Min--5.0-----0,2-
Max0,40.706.0---0.30-0,60.4
Square bars
153250
203555
254060
2842
3045

Round bars

514223038455259
615233139465360
7193075115170260400
8203580120180270440
9214082125185280450
10224585130190290454
11235090135200300500
12245292140210320550
14255595145220320550
152660100150230350
162765105155